Reaction-bonded Silicon Carbide Thermocouple Protection Tube

SiSiC material is made of high-purity silicon carbide powder and Si powder, formed by slip casting, reacted and
 sintered by vacuum furnace. This kiln furniture hase high temperature strength and low mass.
 
 Property
                                                                                                                                                                                                                                                                                                                                                                                                                                   

Item		Technical index
Chemical composition	SiC	≥70
	Si3N4	≥23
Volume density		≥2.46
Apparent porosity		≤16
Crushing strength		≥150
Bending strength	Crashing strength	≥40
	1400℃	≥45
Highest using temperature		1600
Modulus of elasticity		150
Thermal conductivity coefficient		4.4(20-1000℃)
Thermal  conductivity		15(1300℃)

 
 Size available
                                                                                                                                                                                                                                                                                                                                                                                                                                                                                               

OD(mm)	ID(mm)	Max length(mm)
15	9	800
20	13	1000
25	17	1250
30	22	1300
32	24	1300
35	27	1400
38	30	1400
40	30	1500
42	32	1500
45	35	1600
48	36	1700
50	38	1800

 Any other sizes are availabe, pls enquiry for the details.